Red Cast Horseshoe Alnico C-Shape Magnet, AlNiCo U Magnet with N & S Indication, C-shaped U shape Horseshoe Alnico Magnets for Education Physics Experiment Teaching, U-Type Alnico Educational Magnets for Teacher, Al-Ni-Co Horse Shoe Magnet, Industrial Grade Alnico Power Magnet with keeper, Red and Blue Pianted Horseshoe Magnet Supplier Red Cast Horseshoe Alnico C-Shape Magnet […]
Ring NdFeB Magnet Ø6 x Ø2 x 2mm N45 Gold, Sintered Neodymium Customized Ring Craft Magnet, Powerful Rare Earth Permanent Ring Magnet, Sintered Neodymium Iron Boron (NdFeB) magnet, Buy Super Strong Bulk NdFeB Ring Neo Magnets China Supplier & Factory
Ring NdFeB Magnet Ø6 x Ø2 x 2mm N45 Gold Feature:
Plating Gold (Ni-Cu-Ni-Au)
Outer Diameter D 6 mm
Inner Diameter d 2 mm
Volum 50 mm³
Temperature max. 80 °C
Magnetic Grade N45
Tolerance 0.1 mm
Weight 0,00038 kg
Pull Power Force 0,650 kg
Hight H 2 mm
Sintered Neodymium Iron Boron (NdFeB) magnet
Sintered Neodymium Iron Boron (NdFeB), or “neo” magnets, is the third generation of permanent magnet developed in the 1980s. It offers the strongest magnetic power today. With its excellent magnetic characteristics Neodymium Magnet offers flexibility for new designs or is replacing older materials like Alnico and Ceramic in many applications, including high performance motors, brushless DC motors, magnetic separation, magnetic resonance imaging, sensors and loud speakers.
Why Choose Neodymium Magnet
A powder metallurgy process is used in producing sintered Neodymium magnets. Although sintered Neodymium magnet is mechanically stronger than Samarium Cobalt magnets and less brittle than other magnets, it should not be used as a structural component. Selection of Neodymium magnet is limited by temperature due to its irreversible loss and moderately high reversible temperature coefficient of Br and Hcj. The maximum application temperature is 200 °C for high coercivity grades. Neodymium magnet is more prone to oxidation than any other magnet alloys. If Neodymium magnet is to be exposed to humidity, chemically aggressive media such as acids, alkaline solutions salts and harmful gases, coating is recommended. It is not recommended in a hydrogen atmosphere. super strong ndfeb magnet
Neodymium magnet has poor resistance to corrosion and they can also corrode from the inside-out if proper pre-treatment processes are not followed. Oftentimes, multi-layer Nickel-Copper-Nickel plating is applied to prevent failure from corrosion, but this preventative technique may not be sufficient for all applications.
High Anti-corrosion and Low Weight Loss Neodymium Magnet
There are two main standards of low weight loss test as follows:
USA PCT: 121±1℃, 2 atm, 95% RH, 96 hours, weight loss less than 5~10mg/cm2
Europe HAST: 130±2℃, 3 atm, 95% RH, 168 hours, weight loss less than 2~5mg/cm2
Due to special material formulation and manufacturing process, the corrosion resistance is so excellent that neodymium magnet can reach the strict testing requirements above.