WHAT is Sintered Neodymium?
Neodymium magnets are the most widely used magnetic materials available today.
The processing of sintered NdFeB magnet is powder metallurgy. Due to its high Remanence, Coercivity, energy product, small size, light weight, and other special characteristics, the sintered NdFeB magnet can be widely used besides in electro-acoustic components, medical devices, sensors, magnetic separator, magnetic catche, etc. Furthermore, automotive parts, computer hard drives, wind power, power tools, electric bicycles, air conditioning compressor, elevator, aerospace and other fields.
All the NdFeB products that sold by HSMAG Magnet Solutions have been authorized a patent license by the original patent holder, and they can be sold to European and North American market legally.
WHAT is Sintered Neodymium
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
N35
|
Max. 12.1
Min. 11.8
|
Max. 1.21
Min. 1.18
|
Max. 11.4
Min. 11
|
Max. 907
Min. 876
|
Min. 12 / Min. 955
|
Max. 36
Min. 33
|
Max. 287
Min. 263
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N38
|
Max. 12.6
Min. 12.3
|
Max. 1.26
Min. 1.23
|
Max. 11.7
Min. 11.4
|
Max. 931
Min. 907
|
Min. 12 / Min. 955
|
Max. 39
Min. 36
|
Max. 310
Min. 287
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N40
|
Max. 12.9
Min. 12.6
|
Max. 1.29
Min. 1.26
|
Max. 11.9
Min. 11.6
|
Max. 947
Min. 923
|
Min. 12 / Min. 955
|
Max. 41
Min. 38
|
Max. 326
Min. 302
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N42
|
Max. 13.3
Min. 13
|
Max. 1.33
Min. 1.3
|
Max. 12.3
Min. 11.9
|
Max. 979
Min. 947
|
Min. 12 / Min. 955
|
Max. 43
Min. 40
|
Max. 342
Min. 318
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N45
|
Max. 13.6
Min. 13.3
|
Max. 1.36
Min. 1.33
|
Max. 12.1
Min. 11.8
|
Max. 963
Min. 939
|
Min. 12 / Min. 955
|
Max. 46
Min. 43
|
Max. 366
Min. 342
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N48
|
Max. 14
Min. 13.5
|
Max. 1.4
Min. 1.35
|
Max. 12.1
Min. 11.8
|
Max. 963
Min. 939
|
Min. 12 / Min. 955
|
Max. 49
Min. 45
|
Max. 390
Min. 358
|
-0.11
|
-0.6
|
1.05
|
80
|
|
N50
|
Max. 14.2
Min. 13.9
|
Max. 1.42
Min. 1.39
|
Max. 10.5
Min. 9.8
|
Max. 836
Min. 780
|
Min. 11 / Min. 875
|
Max. 50
Min. 47
|
Max. 398
Min. 374
|
-0.11
|
-0.6
|
1.05
|
70
|
|
N53
|
Max. 14.4
Min. 14.4
|
Max. 1.44
Min. 1.42
|
Max. 10.5
Min. 9.8
|
Max. 836
Min. 780
|
Min. 11 / Min. 875
|
Max. 53
Min. 50
|
Max. 421
Min. 398
|
-0.11
|
-0.6
|
1.05
|
70
|
|
N55
|
Max. 14.6
Min. 14.4
|
Max. 1.46
Min. 1.42
|
Max. 10.5
Min. 9.8
|
Max. 836
Min. 780
|
Min. 11 / Min. 875
|
Max. 55
Min. 52
|
Max. 438
Min. 414
|
-0.11
|
-0.6
|
1.05
|
70
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
38M
|
Max. 12.6
Min. 12.3
|
Max. 1.26
Min. 1.23
|
Max. 12.2
Min. 11.7
|
Max. 971
Min. 931
|
Min. 14 / Min. 1114
|
Max. 39
Min. 36
|
Max. 310
Min. 287
|
-0.11
|
-0.59
|
1.05
|
100
|
|
40M
|
Max. 12.9
Min. 12.6
|
Max. 1.29
Min. 1.26
|
Max. 12.3
Min. 11.8
|
Max. 979
Min. 939
|
Min. 14 / Min. 1114
|
Max. 41
Min. 38
|
Max. 326
Min. 302
|
-0.11
|
-0.59
|
1.05
|
100
|
|
42M
|
Max. 13.3
Min. 13
|
Max. 1.33
Min. 1.3
|
Max. 12.4
Min. 12
|
Max. 987
Min. 955
|
Min. 14 / Min. 1114
|
Max. 43
Min. 40
|
Max. 342
Min. 318
|
-0.11
|
-0.59
|
1.05
|
100
|
|
45M
|
Max. 13.6
Min. 13.3
|
Max. 1.36
Min. 1.33
|
Max. 12.1
Min. 11.8
|
Max. 963
Min. 939
|
Min. 14 / Min. 1114
|
Max. 46
Min. 43
|
Max. 366
Min. 342
|
-0.11
|
-0.59
|
1.05
|
100
|
|
48M
|
Max. 13.9
Min. 13.6
|
Max. 1.39
Min. 1.36
|
Max. 12.9
Min. 12.3
|
Max. 1027
Min. 979
|
Min. 14 / Min. 1114
|
Max. 49
Min. 45
|
Max. 390
Min. 358
|
-0.11
|
-0.59
|
1.05
|
100
|
|
50M
|
Max. 14.2
Min. 13.9
|
Max. 1.42
Min. 1.39
|
Max. 13
Min. 11.8
|
Max. 1035
Min. 939
|
Min. 13 /Min. 1035
|
Max. 50
Min. 47
|
Max. 398
Min. 374
|
-0.11
|
-0.59
|
1.05
|
90
|
|
52M
|
Max. 14.4
Min. 14.2
|
Max. 1.44
Min. 1.42
|
Max. 13
Min. 11.8
|
Max. 1035
Min. 939
|
Min. 13 /Min. 1035
|
Max. 52
Min. 49
|
Max. 414
Min. 390
|
-0.11
|
-0.59
|
1.05
|
90
|
|
54M
|
Max. 14.5
Min. 14.3
|
Max. 1.45
Min. 1.43
|
Max. 13
Min. 11.8
|
Max. 1035
Min. 939
|
Min. 13 /Min. 1035
|
Max. 54
Min. 51
|
Max. 430
Min. 410
|
-0.11
|
-0.59
|
1.05
|
90
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
30H
|
Max. 11.2
Min. 10.8
|
Max. 1.12
Min. 1.08
|
Max. 10.7
Min. 10.2
|
Max. 852
Min. 812
|
Min. 17 / Min. 1353
|
Max. 31
Min. 28
|
Max. 247
Min. 223
|
-0.11
|
-0.58
|
1.05
|
120
|
|
35H
|
Max. 12.1
Min. 11.8
|
Max. 1.21
Min. 1.18
|
Max. 11.6
Min. 11.1
|
Max. 923
Min. 884
|
Min. 17 / Min. 1353
|
Max. 36
Min. 33
|
Max. 287
Min. 263
|
-0.11
|
-0.58
|
1.05
|
120
|
|
38H
|
Max. 12.6
Min. 12.3
|
Max. 1.26
Min. 1.23
|
Max. 12.1
Min. 11.7
|
Max. 963
Min. 931
|
Min. 17 / Min. 1353
|
Max. 39
Min. 36
|
Max. 310
Min. 287
|
-0.11
|
-0.58
|
1.05
|
120
|
|
40H
|
Max. 13
Min. 12.6
|
Max. 1.3
Min. 1.26
|
Max. 12.0
Min. 11.5
|
Max. 955
Min. 915
|
Min. 17 / Min. 1353
|
Max. 41
Min. 38
|
Max. 326
Min. 302
|
-0.11
|
-0.58
|
1.05
|
120
|
|
42H
|
Max. 13.1
Min. 12.8
|
Max. 1.31
Min. 1.28
|
Max. 12.0
Min. 11.5
|
Max. 955
Min. 915
|
Min. 16 / Min. 1273
|
Max. 43
Min. 40
|
Max. 342
Min. 318
|
-0.11
|
-0.58
|
1.05
|
120
|
|
44H
|
Max. 13.5
Min. 13.2
|
Max. 1.35
Min. 1.32
|
Max. 12.0
Min. 11.5
|
Max. 955
Min. 915
|
Min. 16 / Min. 1273
|
Max. 45
Min. 42
|
Max. 358
Min. 334
|
-0.11
|
-0.58
|
1.05
|
120
|
|
46H
|
Max. 13.7
Min. 13.4
|
Max. 1.37
Min. 1.34
|
Max. 13.0
Min. 12.6
|
Max. 1035
Min. 1003
|
Min. 16 /Min. 1273
|
Max. 47
Min. 44
|
Max. 374
Min. 350
|
-0.11
|
-0.58
|
1.05
|
120
|
|
48H
|
Max. 13.9
Min. 13.6
|
Max. 1.39
Min. 1.36
|
Max. 13.2
Min. 13
|
Max. 1050
Min. 1035
|
Min. 16 /Min. 1273
|
Max. 48
Min. 45
|
Max. 382
Min. 358
|
-0.11
|
-0.58
|
1.05
|
120
|
|
50H
|
Max. 14.1
Min. 13.8
|
Max. 1.41
Min. 1.38
|
Max. 13.5
Min. 13.1
|
Max. 1074
Min. 1042
|
Min. 16 /Min. 1273
|
Max. 50
Min. 47
|
Max. 398
Min. 374
|
-0.11
|
-0.58
|
1.05
|
110
|
|
52H
|
Max. 14.4
Min. 14.2
|
Max. 1.44
Min. 1.42
|
Max. 13.8
Min. 13.5
|
Max. 1098
Min. 1074
|
Min. 16 /Min. 1273
|
Max. 52
Min. 49
|
Max. 414
Min. 398
|
-0.11
|
-0.58
|
1.05
|
110
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
30SH
|
Max. 11.2
Min. 10.8
|
Max. 1.12
Min. 1.08
|
Max. 10.7
Min. 10.2
|
Max. 852
Min. 812
|
Min. 20 / Min. 1592
|
Max. 31
Min. 28
|
Max. 247
Min. 223
|
-0.11
|
-0.55
|
1.05
|
150
|
|
35SH
|
Max. 12
Min. 11.7
|
Max. 1.2
Min. 1.17
|
Max. 11.6
Min. 11.1
|
Max. 923
Min. 884
|
Min. 20 / Min. 1592
|
Max. 36
Min. 33
|
Max. 287
Min. 263
|
-0.11
|
-0.55
|
1.05
|
150
|
|
38SH
|
Max. 12.6
Min. 12.3
|
Max. 1.26
Min. 1.23
|
Max. 12.1
Min. 11.7
|
Max. 963
Min. 931
|
Min. 20 / Min. 1592
|
Max. 39
Min. 36
|
Max. 310
Min. 287
|
-0.11
|
-0.55
|
1.05
|
150
|
|
40SH
|
Max. 13.0
Min. 12.6
|
Max. 1.30
Min. 1.26
|
Max. 12.3
Min. 12.0
|
Max. 979
Min. 955
|
Min. 20 / Min. 1592
|
Max. 41
Min. 38
|
Max. 326
Min. 302
|
-0.11
|
-0.55
|
1.05
|
150
|
|
42SH
|
Max. 13.1
Min. 12.8
|
Max. 1.31
Min. 1.28
|
Max. 12.4
Min. 12.1
|
Max. 987
Min. 963
|
Min. 20 / Min. 1592
|
Max. 43
Min. 40
|
Max. 342
Min. 318
|
-0.11
|
-0.55
|
1.05
|
150
|
|
44SH
|
Max. 13.5
Min. 13.2
|
Max. 1.35
Min. 1.32
|
Max. 12.8
Min. 12.4
|
Max. 1019
Min. 987
|
Min. 20 / Min. 1592
|
Max. 45
Min. 42
|
Max. 358
Min. 334
|
-0.11
|
-0.55
|
1.05
|
150
|
|
45SH
|
Max. 13.6
Min. 13.3
|
Max. 1.36
Min. 1.33
|
Max. 13.2
Min. 12.8
|
Max. 1050
Min. 1019
|
Min. 20 /Min. 1592
|
Max. 46
Min. 43
|
Max. 366
Min. 342
|
-0.11
|
-0.55
|
1.05
|
150
|
|
48SH
|
Max. 13.9
Min. 13.6
|
Max. 1.39
Min. 1.36
|
Max. 13.5
Min. 13.2
|
Max. 1074
Min. 1050
|
Min. 20 /Min. 1592
|
Max. 48
Min. 45
|
Max. 382
Min. 358
|
-0.11
|
-0.55
|
1.05
|
150
|
|
50SH
|
Max. 14.2
Min. 14.0
|
Max. 1.42
Min. 1.40
|
Max. 13.8
Min. 13.5
|
Max. 1098
Min. 1074
|
Min. 20 /Min. 1592
|
Max. 50
Min. 47
|
Max. 398
Min. 374
|
-0.11
|
-0.55
|
1.05
|
150
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
28UH
|
Max. 10.9
Min. 10.5
|
Max. 1.09
Min. 1.05
|
Max. 10.4
Min. 10
|
Max. 828
Min. 796
|
Min. 25 / Min. 1989
|
Max. 29
Min. 26
|
Max. 231
Min. 207
|
-0.11
|
-0.51
|
1.05
|
180
|
|
30UH
|
Max. 11.2
Min. 10.8
|
Max. 1.12
Min. 1.08
|
Max. 10.3
Min. 10
|
Max. 820
Min. 796
|
Min. 25 / Min. 1989
|
Max. 31
Min. 28
|
Max. 247
Min. 223
|
-0.11
|
-0.51
|
1.05
|
180
|
|
33UH
|
Max. 11.5
Min. 11.1
|
Max. 1.15
Min. 1.11
|
Max. 10.8
Min. 10.5
|
Max. 860
Min. 836
|
Min. 25 / Min. 1989
|
Max. 34
Min. 31
|
Max. 271
Min. 247
|
-0.11
|
-0.51
|
1.05
|
180
|
|
35UH
|
Max. 12.0
Min. 11.7
|
Max. 1.20
Min. 1.17
|
Max. 11.6
Min. 11.1
|
Max. 923
Min. 884
|
Min. 25 / Min. 1989
|
Max. 36
Min. 33
|
Max. 287
Min. 263
|
-0.11
|
-0.51
|
1.05
|
180
|
|
38UH
|
Max. 12.6
Min. 12.3
|
Max. 1.26
Min. 1.23
|
Max. 12.1
Min. 11.7
|
Max. 963
Min. 931
|
Min. 25 / Min. 1989
|
Max. 38
Min. 35
|
Max. 302
Min. 287
|
-0.11
|
-0.51
|
1.05
|
180
|
|
39UH
|
Max. 12.7
Min. 12.4
|
Max. 1.27
Min. 1.24
|
Max. 12.1
Min. 11.7
|
Max. 963
Min. 931
|
Min. 25 / Min. 1989
|
Max. 39
Min. 36
|
Max. 302
Min. 286
|
-0.11
|
-0.51
|
1.05
|
180
|
|
40UH
|
Max. 13.0
Min. 12.6
|
Max. 1.30
Min. 1.26
|
Max. 12.3
Min. 12.0
|
Max. 979
Min. 955
|
Min. 25 / Min. 1989
|
Max. 41
Min. 38
|
Max. 326
Min. 302
|
-0.11
|
-0.51
|
1.05
|
180
|
|
42UH
|
Max. 13.1
Min. 12.8
|
Max. 1.31
Min. 1.28
|
Max. 12.4
Min. 12.1
|
Max. 987
Min. 963
|
Min. 25 / Min. 1989
|
Max. 42
Min. 39
|
Max. 334
Min. 302
|
-0.11
|
-0.51
|
1.05
|
180
|
|
45UH
|
Max. 13.5
Min. 13.2
|
Max. 1.35
Min. 1.32
|
Max. 12.8
Min. 12.4
|
Max. 1019
Min. 987
|
Min. 25 /Min. 1989
|
Max. 45
Min. 42
|
Max. 358
Min. 334
|
-0.11
|
-0.51
|
1.05
|
180
|
|
48UH
|
Max. 13.8
Min. 13.6
|
Max. 1.38
Min. 1.36
|
Max. 13.2
Min. 12.8
|
Max. 1050
Min. 1019
|
Min. 25 /Min. 1989
|
Max. 49
Min. 45
|
Max. 390
Min. 358
|
-0.11
|
-0.51
|
1.05
|
180
|
|
50UH
|
Max. 14.0
Min. 13.8
|
Max. 1.40
Min. 1.38
|
Nom. 13.1
Min. 13
|
1073 Nom.
|
Min. 25 /Min. 1990
|
Max. 50
Min. 48
|
Max. 398
Min. 382
|
-0.11
|
-0.51
|
1.05
|
180
|
|
52UH
|
Max. 14.3
Min. 14
|
Max. 1.43
Min. 1.40
|
Nom. 13.4
Min. 13.2
|
1103 Nom.
|
Min. 24.5 /Min. 1950
|
Max. 51.5
Min. 50
|
Max. 410
Min. 398
|
-0.11
|
-0.51
|
1.05
|
180
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
30EH
|
Max. 11.2
Min. 10.8
|
Max. 1.12
Min. 1.08
|
Max. 10.3
Min. 10
|
Max. 820
Min. 796
|
Min. 30 / Min. 2387
|
Max. 31
Min. 28
|
Max. 247
Min. 223
|
-0.11
|
-0.48
|
1.05
|
200
|
|
33EH
|
Max. 11.5
Min. 11.1
|
Max. 1.15
Min. 1.11
|
Max. 10.8
Min. 10.5
|
Max. 860
Min. 836
|
Min. 30 / Min. 2387
|
Max. 34
Min. 31
|
Max. 271
Min. 247
|
-0.11
|
-0.48
|
1.05
|
200
|
|
35EH
|
Max. 12.2
Min. 11.7
|
Max. 1.22
Min. 1.17
|
Max. 11.6
Min. 11.1
|
Max. 923
Min. 884
|
Min. 30 / Min. 2387
|
Max. 36
Min. 33
|
Max. 287
Min. 263
|
-0.11
|
-0.48
|
1.05
|
200
|
|
38EH
|
Max. 12.5
Min. 12.3
|
Max. 1.25
Min. 1.23
|
Max. 11.8
Min. 11.6
|
Max. 931
Min. 891
|
Min. 30 / Min. 2387
|
Max. 38
Min. 35
|
Max. 302
Min. 287
|
-0.11
|
-0.48
|
1.05
|
200
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
30AH
|
Max. 11.2
Min. 10.8
|
Max. 1.12
Min. 1.08
|
Max. 10.3
Min. 10
|
Max. 820
Min. 796
|
Min. 35 / Min. 2786
|
Max. 31
Min. 28
|
Max. 247
Min. 223
|
-0.09
|
-0.43
|
1.05
|
230
|
|
33AH
|
Max. 11.5
Min. 11.1
|
Max. 1.15
Min. 1.11
|
Max. 10.8
Min. 10.5
|
Max. 860
Min. 836
|
Min. 35 / Min. 2786
|
Max. 34
Min. 31
|
Max. 271
Min. 247
|
-0.09
|
-0.43
|
1.05
|
230
|
GRADE |
REMANENCE FLUX DENSITY |
COERCIVITY FORCE |
MAX. ENERGY PRODUCT |
TEMP. COEF. |
RELATIVE RECOIL PERMEABILITY |
MAX WORK TEMP. |
|||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Br
|
Hcb
|
Hcj
|
(BH)max
|
αBr
|
βHcj
|
||||||
|
KGs
|
T
|
KOe
|
KA/m
|
KOe KA/m
|
MGOe
|
KJ/m3
|
(%/°C)
|
(%/°C)
|
μrec
|
L/D≥0.7 (°C)
|
|
|
35HP
|
Max. 12.2
Min. 11.9
|
Max. 1.22
Min. 1.19
|
Max. 11.7
Min. 11.2
|
Max. 931
Min. 891
|
Min. 16 / Min. 1273
|
Max. 37
Min. 34
|
Max. 295
Min. 272
|
-0.11
|
-0.6
|
1.05
|
110
|
|
38HP
|
Max. 12.7
Min. 12.4
|
Max. 1.27
Min. 1.24
|
Max. 12.2
Min. 11.8
|
Max. 971
Min. 939
|
Min. 16 / Min. 1273
|
Max. 40
Min. 37
|
Max. 318
Min. 296
|
-0.11
|
-0.6
|
1.05
|
110
|
|
40HP
|
Max. 12.9
Min. 12.6
|
Max. 1.29
Min. 1.26
|
Max. 12.3
Min. 12
|
Max. 979
Min. 955
|
Min. 16 / Min. 1273
|
Max. 42
Min. 39
|
Max. 334
Min. 312
|
-0.11
|
-0.6
|
1.05
|
110
|
Physical Characteristics
No.
Item
Value
1
Density
7.4~7.7g/cm³
2
Compressive Strength
1000~1200MPa
3
Modulus of elasticity
140~160GPa
4
Curie temp
300~350°C
5
Electrical resistivity
130~160Ω.cm
6
Coefficient of thermal expansion
| -2.5~-2.8×10-6/°C
| |5.5~-6.8×10-6/°C
7
Thermal Conductivity
| 7.5W/(m.k.)
| |6.5W/(m.k.)
8
Vickers Hardness
600~620Hv
Sintered Neodymium N40 Conical Taper Magnets
HDD Head-Actuator Rare Earth Sintered Neodymium Magnet
Sintered Neodymium Circular Ring Drive Pump Magnets N38
Sintered Neodymium Wedge Magnet for Wind Generator
Super Strong N50 Sintered Neodymium Magnet Block Square
Powerful Sintered Neodymium Micro Sensor Magnets Ф1.5*Ф1.0*5.2mm